Kpochapụ Cross Linked Pof Shrink Film Polyolefin Pof Shrink Film
Kedu ụdị ihe nkiri POF na-ebelata ihe nkiri dị?
Enwere ụdị ihe nkiri POF na-ebelata anọ dị n'ahịa:
1.POF Shrink Film Regular: Nke a bụ ihe nkiri na-ebelata ọkọlọtọ nke a na-ejikarị emepụta ngwaahịa iji chebe elu ngwaahịa. Ihe nkiri ahụ n'onwe ya enweghị ihe ndị a ma ama; ọ dị gịrịgịrị, doo anya, yana enyi na gburugburu ebe obibi. Kwesịrị ekwesị maka nkwakọ ngwaahịa izugbe dị ka igbe ịchọ mma, igbe mgbakwunye nri, akwụkwọ, yogọt, mmiri ara ehi utoojoo, na ihe ndị ọzọ.
2.POF Shrink Film Cross-Linked: Na-esote bụ ihe nkiri POF na-ebelata nke na-agafe usoro njikọ njikọ, nke na-eme ka ike na ịdịte aka nke ihe nkiri ahụ dịkwuo elu. Ọ naghị adọkasị ngwa ngwa, na-ejigide ihe ndị na-ebelata ya, ma ọ ka dị gịrịgịrị ma doo anya. Kwesịrị ekwesị maka ngwaahịa nwere ụdị pụrụ iche dị ka bọọlụ.
3.POF Shrink Film High Performance: Ihe nkiri POF a na-eme ka ọ dị elu nwere àgwà dị elu nke kwesịrị ekwesị maka ngwa ngwa ngwa ngwa ngwa ngwa ngwa ngwa. Ọ nwere akara akara siri ike, na-eme ka ọ dabara maka ngwaahịa noodle emechara ọkara.
4.POF Shrink Film Anti-Fog: N'ikpeazụ, a na-emepụta ihe nkiri POF a na-akụda nke ọma iji gbochie foogu ma ọ bụ condensation na-emepụta na ngwaahịa ahụ, karịsịa maka ihe oriri ọhụrụ dị ka akwụkwọ nri, mkpụrụ osisi, anụ, na oyi kpọnwụrụ njikere iri nri.
Ngwa ngwaahịa
Okpokoro | Ogologo (M) | Obosara (MM) | ||||||
BRJ03 | SW | CF | SW | CF | ||||
12 | 10002/6680/3334 | 1667 | 200-3200 | 150-1000 | ||||
15 | 7992/5328/2664 | 1332 | ||||||
19 | 6402/4268/2134 | 1067 | ||||||
25 | 4800/3200/1600 | 800 | ||||||
30 | 3996/2664/1332 | 666 | ||||||
38 | 3156/2104/1052 | 526 | ||||||
NJ isi akwụkwọ | 76/152 | 76 | 76/152 | 76 | ||||
Ihe nkiri Polyolefin Shrink | ||||||||
BRJ-03 | ||||||||
Nnwale ihe | UNIT | Nnwale ASTM | URU NDỊ MMADỤ | |||||
Okpokoro | micron | 12 | 15 | 19 | 25 | 30 | 38 | |
OPTIC | ||||||||
Ofufe | D1003 | 2.2 | 2.5 | 3 | 3.7 | 4.3 | 4.5 | |
Ido anya | D1746 | 87 | 87 | 87 | 87 | 87 | 87 | |
Gloss@45Deg | D2457 | 94 | 94 | 91 | 87 | 76 | 75 | |
AKWỤKWỌ MMADỤ | MD | TD | MD | TD | ||||
Mbelata 100 ℃ efu | % | D2732 | 15 | 25 | 15 | 25 | ||
Mbelata 110 ℃ efu | % | D2732 | 35 | 45 | 30 | 40 | ||
Mbelata 120 ℃ efu | % | D2732 | 68 | 70 | 65 | 66 | ||
Mbelata 130 ℃ efu | % | D2732 | 81 | 80 | 80 | 79 | ||
TENSILE | ||||||||
Ike tensile (MD) | D882 | 120 | 100 | |||||
Ike Tensile (TD) | 130 | 110 | ||||||
elongation(MD) | % | 120 | 130 | |||||
Elongation(TD) | 120 | 130 | ||||||
Ike akara | ||||||||
MD/ọkụ waya akara | N/15mm | F88 | 12.5 | 15.2 | 18.5 | 12.5 | 15.2 | 18.5 |
TD/ Hot waya akara | 13 | 16.6 | 19 | 13 | 16.6 | 19 | ||
COF (ihe nkiri na ihe nkiri) | ||||||||
Dị ike | D1894 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | |
Static | 0.21 | 0.21 | 0.21 | 0.21 | 0.21 | 0.21 | ||
Oke nchekwa nchekwa | ℃ | 32 |